From the results show that compressive strength of concrete with quarry dust as aggregates is the highest with 30.82 MPa with density 2251.85 kg/m 3. This show, ceramic waste and quarry dust can be alternative …
The combined use of silica fume (SF) and ceramic waste (CW) for the production of mortar is studied. Sand is replaced by 5%, 10%, 15% and 20% of CW while a fixed 5% percentage (% wt of cement) of ...
Senthamarai, RM.; Devadas Manhoharan, P. Concrete with ceramic waste aggregate. Cement and Concrete Composites, 27(9-10) 910-913, 2005. F. Pacheco-Torgal, S. Jalali "Reusing ceramic wastes in concrete" …
Concrete made with ceramic electrical insulator waste as coarse aggregate shows good workability, compressive, tensile and flexural strengths and modulus of elasticity. Further, study of its durability will ensure greater reliability in its usage. Permeation characters are used widely to quantify durability properties of concrete.
HPC was prepared for various cement contents ranging from 300 kg/m 3 to 500 kg/ m 3 by replacing 10% of the volume of the cement by silica fume and 40% of the volume of the fine aggregate by ...
Numerous researchers, such as Senthamarai & Devadas-Manoharan (2005) and Suzuki et al. (2009), identified that ceramics have the potential to replace natural aggregates. Furthermore, Cristiano ...
38 M. Purushothaman & RM. Senthamarai Test Specimens For each mix, six cubes of size 100 mm × 100 mm were cast to determine compressive strength, splitting tensile strength; three beams of size 100 × 100 × 500 mm were cast for flexural strength and three cubes of size 150 mm × 150 mm were cast to determine the modulus of elasticity.
M. Sneha, RM. Senthamarai Abstract: Use of agro and industrial wastes in concrete production will cause sustainable concrete era and greener habitat. In this study an endeavor has been made to discover the propriety of Sugarcane Bagasse Ash (SCBA) and Granite Waste (GW) as partial replacement for traditional river sand. The
Purushothaman MP, Professor (Associate) | Cited by 18 | of Annamalai University, Annāmalainagar | Read 5 publications | Contact Purushothaman MP
Present Address: Contact Number: E-Mail Address: No.90 Vagesh Nagar, Chidambaram - 608 001. 9443405809: dgnath008@gmail
M Sneha RM Senthamarai, "Use of Bagasse Ash as Pozzolanic material in concrete - A Review.", International Journal of Advance and Innovation Research, Volume 5, Number …
Senthamarai et al. [18] noted the durability of concrete mixtures having waste ceramic electrical insulators as coarse aggregate substitution from six different w/c ratios (0.35 to 0.60 with an ...
RM. Senthamarai, P. Devadas Manoharan / Cement & Concrete Composites 27 (2005) 910–913 911. coarse aggregate concrete and conventional concrete are very small. Fig. 2 shows the stress–strain behavior of ceramic waste coarse aggregate concrete. The modulus of elastic- ity of ceramic waste coarse aggregate concrete varied from 22 to 16 …
Rm. Senthamarai; Devadas Manoharan P; Use of hazardous industrial wastes in concrete-making will lead to greener environment. In ceramic industry about 30% production goes as waste, which is not ...
M Sneha RM Senthamarai, "Use of Bagasse Ash as Pozzolanic material in concrete - A Review.", International Journal of Advance and Innovation Research, Volume 5, Number 3(III), 2018, pp. 13-24. 2018. M Sneha RM Senthamarai, "Design and Performance of Sustainable Concrete.", International Journal of Applied Engineering Research, Volume …
RM. Senthamarai, P. Devadas Manoharan / Cement & Concrete Composites 27 (2005) 910–913 911. 4. Discussion. 4.1. Properties of ceramic waste coarse …
Concrete which contains waste products as aggregate is called 'Green' concrete. Use of hazardous waste in concrete-making will lead to green environment and …
mns0138:2010 "Керамик тоосго ба гулдмай" техникийн шаардлага, mns831:2001 "Сийрмэг бетон. Бүтээц ба эдлэхүүн" техникийн шаардлага, mns6054:2009 "Ханын бетон гулдмай". Техникийн ерөнхий шаардлага,
RM Senthamarai, university ranking, university rankings, world university ranking, world university ranking Created Date: 3/9/2022 4:47:40 PM ...
RM. Senthamarai, P. Devadas Manoharan / Cement & Concrete Composites 27 (2005) 910–913 911. 4. Discussion 4.1. Properties of ceramic waste coarse aggregate ...
Ceramic dust is produced as waste from ceramic bricks, roof and floor tiles and stoneware waste industries. Concrete (M35) was made by replacing % (up to 30%) of cement (OPC 53) grade with ceramic dust (passing 75µm) shows good workability, compressive strength, split-tensile strength, flexural strength and elastic modulus. In this experimental …
Rm. Senthamarai; Devadas Manoharan P; D. Gobinath; Concrete which contains waste products as aggregate is called 'Green' concrete. Use of hazardous waste in concrete-making will lead to green ...
Concrete with ceramic waste aggregate RM.Senthamarai, P. Devadas Manoharan India Received 20 August 2003; accepted 4 April 2005 Available online 13 June 2005 . [3] 11 nov 2015 by Parminder Singh department of civil engineering Giani Zail Singh Punjab Technical University Campus and Dr. Rakesh Kumar Singla Associate ProfessorDepartment of ...
Dr. RM.Senthamarai Professor Department of Civil & Structural Engineering Annamalai University Introduction Concrete mix proportioning or Mix Design is a process that …
The ceramic electrical insulator waste (Fig. 1) was procured from the nearby ceramic electrical insulator industry and their surfaces were de-glazed manually by chisel and hammer.With the help of jaw crusher the de-glazed ceramic electrical insulator wastes were broken into 20 mm maximum size coarse aggregate (Fig. 2), the same was used as …
Senthamarai et al. [18] noted the durability of concrete mixtures having waste ceramic electrical insulators as coarse aggregate substitution from six different w/c ratios …
RM Senthamarai, PD Manoharan, D Gobinath. Construction and Building Materials 25 (5), 2413-2419, 2011. 255: 2011: Strength properties of high performance concrete using …
Concrete with ceramic waste aggregate RM.Senthamarai, P. Devadas Manoharan India Received 20 August 2003; accepted 4 April 2005 Available online 13 June 2005 . [3] 11 nov 2015 by Parminder Singh department of …
M. PURUSHOTHAMAN & RM. SENTHAMARAI" Department of Structural Engineering, Annamalai University, Chidambaram, Tamil Nadu, India 11. Show More. Related. Unbroken Essay 749 Words | 3 Pages. Unbroken is a biography by Laura Hillenbrand about Louie Zamperini's entire life. Louie Zamperini is a son of Italian Immigrants that moved to …
Six ceramic waste coarse aggregate concrete mixes were designed by the volumetric method with different water–cement ratios (0.35, 0.40, 0.45, 0.50, 0.55 and 0.60). Similarly, six more conventional concrete mixes were designed with crushed stone coarse aggregate. The volume of individual ingredients was the same in both the ceramic waste ...
Sentharamai (2005): Senthamarai concluded that ceramic tile waste can be effectively used as aggregates in concrete making, due to its strength. He found out that the crushing value as 27, impact value as 21, abrasion value was 28% for ceramic and for natural coarse aggregate these were 24, 17 and 20% respectively. ... New Delhi, India. [2 ...
Numerous researchers, such as Senthamarai & Devadas-Manoharan (2005) and Suzuki et al. (2009), identified that ceramics have the potential to replace …
Rm. Senthamarai; Devadas Manoharan P; Use of hazardous industrial wastes in concrete-making will lead to greener environment. In ceramic industry about 30% production goes as waste, which is not ...
Dr. RM.Senthamarai Professor Department of Civil & Structural Engineering Annamalai University Introduction Concrete mix proportioning or Mix Design is a process that consists of two interrelated steps: (1) selection of the suitable ingredients and (2) determination of their relative quantities to produce, as economically as possible, concrete ...
We found Senthamarai. Fast and FREE people search provides current address, phone, email, relatives, criminal records, public records & more. FREE!